| 9SvMn Pb36k |
|---|
Round Bar
Chemical Composition |
| Carbon | 0,15 |
| Silicon | 0,05 |
| Manganese | 1.10 - 1.50 |
| Phosphorus | 0,1 |
| Sulphur | 0.34 - 0.40 |
| Lead | 0.15 - 0.35 |
| SIZE | KG/M |
| 6 | 0,222 |
| 7 | 0,302 |
| 8 | 0,395 |
| 9 | 0,499 |
| 10 | 0,617 |
| 11 | 0,746 |
| 12 | 0,888 |
| 13 | 1,042 |
| 14 | 1,175 |
| 15 | 1,387 |
| 16 | 1,578 |
| 18 | 1,998 |
| 20 | 2,466 |
| 22 | 2,984 |
| 24 | 3,551 |
| 25 | 3,853 |
| 26 | 4,168 |
| 27 | 4,495 |
| 28 | 4,824 |
| 30 | 5,549 |
| 32 | 6,313 |
| 35 | 7,553 |
| 36 | 7,99 |
| 38 | 8,903 |
| 40 | 9,865 |
| 45 | 12,485 |
| 50 | 15,413 |
| 55 | 18,65 |
MECHANICAL PROPERTIES:
Several have verified that there is no significant or discernible difference in static strength, ductility or notch sensitiviity between fine grained
leaded carbon steels and their non leaded counterparts.
Leaded free cutting imported bright material
Pre chamfered both ends
TYPICAL USES :
For high speed production of repition work (e.g. manufacture of bushes, pins, bolts, studs and couplings) where the major requirements are rapid
machining and maximum tool life.
Cutting speeds and feeds can be increased considerably due to the higher lead content.
FABRICATION :
All reports have indicated that the leaded grades can be forged, cold forged, swaged, welded, brazed and soldered as well as similar non leaded grades